|Nominal Resin Properties(1,2)||Value (SI Units)||Method|
|Density||0.946 g/cm3||ASTM D1505|
|Melt Index,Condition 190°C / 2.16 kg||0.18 g/10 min||ASTM D1238|
|Brittleness Temperature, Type A clamp, Type I specimen||<-75°C||ASTM D746|
|ESCR,Condition B (100% Igepal), F50||>1000 hrs||ASTM D1693|
|Flexural Modulus, Tangent - 16:1 span:depth, 12.7 mm/min||1150 MPa||ASTM D790|
|Nominal Blown Film Properties at 0.025mm(1,3)||Value (SI Units)||Method|
|Dart Drop (66 cm)||90 g||ASTM D1709|
|Tensile Strength at Yield, 50.8 mm/min MD||24 MPa||ASTM D882|
|Tensile Strength at Yield, 50.8 mm/min TD||26 MPa||ASTM D882|
|Elongation at Break, 50.8 mm/min MD||480%||ASTM D882|
|Elongation at Break, 50.8 mm/min TD||640%||ASTM D882|
|Elmendorf Tear Strength,MD||19 g||ASTM D1922|
|Elmendorf Tear Strength,TD||270 g||ASTM D1922|